Electrochemomechanical failure in layered oxide cathodes caused by rotational stacking faults

Abstract

Electrochemomechanical degradation is one of the most common causes of capacity deterioration in high-energy-density cathodes, particularly intercalation-based layered oxides. Here we reveal the presence of rotational stacking faults (RSFs) in layered lithium transition-metal oxides, arising from specific stacking sequences at different angles, and demonstrate their critical role in determining structural/electrochemical stability. Our combined experiments and calculations show that RSFs facilitate oxygen dimerization and transition-metal migration in layered oxides, fostering microcrack nucleation/propagation concurrently with cumulative electrochemomechanical degradation on cycling. We further show that thermal defect annihilation as a potential solution can suppress RSFs, reducing microcracks and enhancing cyclability in lithium-rich layered cathodes. The common but previously overlooked occurrence of RSFs suggests a new synthesis guideline of high-energy-density layered oxide cathodes. © The Author(s), under exclusive licence to Springer Nature Limited 2024.